Structural and Electrical Characterization of Bi2Se3 Nanostructures Grown by Metalorganic Chemical Vapor Deposition

Abstract

We characterize nanostructures of Bi2Se3 that are grown via metalorganic chemical vapor deposition using the precursors diethyl selenium and trimethyl bismuth. By adjusting growth parameters, we obtain either single-crystalline ribbons up to 10 microns long or thin micron-sized platelets. Four-terminal resistance measurements yield a sample resistivity of 4 mOhm-cm. We observe weak anti-localization and extract a phase coherence length l_phi = 178 nm and spin-orbit length l_so = 93 nm at T = 0.29 K. Our results are consistent with previous measurements on exfoliated samples and samples grown via physical vapor deposition.