Magnetically active vacancy related defects in irradiated GaN layers
Abstract
We present the studies of magnetic properties of 2 MeV 4He+-irradiated GaN grown by metal-organic chemical-vapor deposition. Particle irradiation allowed controllable introduction of Ga-vacancy in the samples. The magnetic moments with concentrations changing between 4.3...8.3x1017 cm-3 showing superparamagnetic blocking at room temperature are observed. The appearance of clear hysteresis curve at T = 5 K with coercive field of about HC = 270 Oe suggests that the formation of more complex Ga vacancy related defects is promoted with increasing Ga vacancy content. The small concentration of the observed magnetically-active defects with respect to the total Ga- vacancy concentration suggests that the presence of the oxygen/hydrogen-related vacancy complexes is the source of the observed magnetic moments.
Turn this paper into a lesson
ArcXiv compiles a structured reading guide from this paper's metadata: plain-English importance, contributions, prerequisite concepts, which sections to read first, flashcards, and a quiz. Grounded in the abstract, never invented.