Interface observation of heat-treated Co/Mo2C multilayers
Abstract
We study the interface evolution of a series of periodic Co/Mo2C multilayers as a function of the annealing temperature up to 600C. Different complementary techniques are implemented to get information on the phenomenon taking place at the interfaces of the stack. The periodical structure of Co/Mo2C multilayer is proven by Time-of-flight secondary ion mass spectrometry (ToF-SIMS) depth profiles which demonstrate the formation of an oxide layer at both air/stack and stack/substrate interfaces. From Nuclear magnetic resonance (NMR) spectra, we observed the intermixing phenomenon of Co and C atoms for the as-deposited sample, and then at annealing temperature above 300C Co and C atoms separate from their mixed regions. Comparison of NMR results between Co/Mo 2 C and Co/C references confirms this phenomenon. This is in agreement with x-ray emission spectroscopy (XES) measurements. Furthermore the calculation of the Co-C, Co-Mo and Mo-C mixing enthalpy using Miedema's model gives a proof of the demixing of Co and C atoms present within the stacks above 300C. From the transmission electron microscopy (TEM) analysis, we found the presence of some crystallites within the as-deposited sample as well as the mainly amorphous nature of all layers. This is confirmed using x-ray diffraction (XRD) patterns which also demonstrate the growth of crystallites induced upon annealing.
Turn this paper into a lesson
ArcXiv compiles a structured reading guide from this paper's metadata: plain-English importance, contributions, prerequisite concepts, which sections to read first, flashcards, and a quiz. Grounded in the abstract, never invented.