Oxygen-annealing effects on superconductivity in polycrystalline Fe1-xTe1-ySey
Abstract
Superconductivity in anti-PbO-type iron chalcogenides Fe1-xTe1-ySey (x = 0, 0.1, y = 0.1 0.4) depends on the amount (x) of interstitial iron atoms located between the FeTe1-ySey layers. Non-superconducting samples of nominal Fe1.1Te1-ySey convert to superconductors with critical temperatures up to 14 K after annealing at 300C in an oxygen atmosphere. The process is irreversible upon subsequent hydrogen annealing. Magnetic measurements are consistent with the formation of iron oxides suggesting that oxygen annealing preferably extracts interstitial iron from Fe1-xTe1-ySey which interfere with superconductivity.