Growth, Crystal Structure and Magnetic Characterization of Zn-Stabilized CePtIn4
Abstract
The growth and characterization of CePtIn4, stabilized by 10% Zn substitution for In, is reported. The new material is orthorhombic, space group Cmcm (No. 63), with lattice parameters a = 4.51751(4) , b = 16.7570(2) , and c = 7.36682(8) , and the refined crystal composition has 10% of Zn substituted for In, i.e. the crystals are CePt(In3.6Zn0.1)4. Crystals were grown using a self-flux method: only growths containing Zn yielded CePtIn4 crystals, while Ce3Pt4In13 crystals formed when Zn was not present. Anisotropic temperature-dependent magnetic susceptibilities for single crystals show that Zn-stabilized CePtIn4 orders magnetically at ~1.9 K. High-temperature Curie-Weiss fits indicate an effective moment of ~2.30 muB/ Ce and a directionally averaged Weiss-temperature of approximately - 9 K. Specific heat data shows a peak consistent with the ordering temperature seen in the magnetic susceptibility data. Zn-stabilized CePtIn4 is metallic and displays no superconducting transition down to 0.14 K.
Turn this paper into a lesson
ArcXiv compiles a structured reading guide from this paper's metadata: plain-English importance, contributions, prerequisite concepts, which sections to read first, flashcards, and a quiz. Grounded in the abstract, never invented.