Growth and Characterization of Fe0.95Se0.6Te0.4 Single Crystal
Abstract
In this paper we present the single crystal growth of Fe0.95Se0.6Te0.4 high TC superconducting sample by the modified Bridgman technique. The x-ray diffraction pattern shows the single crystal nature of the sample, as only (00l) peaks are detectable. The stoichiometric composition has been verified by energy dispersive x-ray analysis. The superconducting transition temperature at 14 K was confirmed through DC magnetization (ZFC-FC) and resistivity measurements. By analyzing the isothermal M-H curves, we determined the value of Hc1 (0) ~360 Oe by extrapolating the data. The temperature coefficient of resistivity obtained using the power law fitting was found to be 0.6. The obtained Raman spectra at room temperature can be interpreted with the tetragonal crystal structure and space group P4/nmm.
Turn this paper into a lesson
ArcXiv compiles a structured reading guide from this paper's metadata: plain-English importance, contributions, prerequisite concepts, which sections to read first, flashcards, and a quiz. Grounded in the abstract, never invented.