Microstructure evolution and densification during spark plasma sintering of nanocrystalline W-5wt.%Ta alloy
Abstract
The present work reports the effect of Ta on densification and microstructure evolution during non-isothermal and spark plasma sintering of nanocrystalline W. Nanocrystalline W-5wt.%Ta alloy powder was synthesized using mechanical alloying. The nanocrystalline powder was characterized thoroughly using X-ray diffraction line profile analysis. Furthermore, the shrinkage behavior of nanocrystalline powder was investigated during non-isothermal sintering using dilatometry. Subsequently, the alloy powder was consolidated using spark plasma sintering up to 1600 C. The role of Ta on stabilizing the microstructure during spark plasma sintering of nanocrystalline W was investigated in detail using electron backscatter diffraction. The average grain size of spark plasma sintered W-5wt.%Ta alloy was observed as 1.73 micron.