Carbon deposition on hematite (α-Fe2O3) nanocubes by an annealing in the air: morphology study with grazing incidence small angle X-ray scattering (GISAXS)
Abstract
GISAXS has been used to study morphology change of α-Fe2O3 nanocubes after annealing processes. A submonolayer of the nanocubes was deposited on a Si(100) substrate. While an annealing at 400 in a vacuum does not change a GISAXS pattern from as-prepared nanocubes submonolayer, annealing in the air at the same temperature altered the GISAXS pattern significantly. SEM image showed that the air-annealed nanocubes were coated with thin layers which were identified as amorphous carbon layers based on Raman measurements. GISAXS simulations from morphologies of nanocube with 38 nm side-length and core-shell (nanocube-core and 7 nm thick carbon-shell) nicely reproduced measured patterns from the vacuum annealed and the air-annealed nanocubes, respectively. The current study provides new approach for in-situ characterization of carbon deposition on a uniform shape nanoparticle through monitoring of deposited carbon thickness.