Degradation model of high-nickel positive electrodes: Effects of loss of active material and cyclable lithium on capacity fade

Abstract

Nickel-rich layered oxides have been widely used as positive electrode materials for high-energy-density lithium-ion batteries, but their degradation has severely affected cell performance, in particular at a high voltage and temperature. However, the underlying degradation mechanisms have not been well understood due to the complexity and lack of predictive models.Here we present a model at the particle level to describe the structural degradation caused by phase transition in terms of loss of active material (LAM), loss of lithium inventory (LLI), and resistance increase. The particle degradation model is then incorporated into a cell-level P2D model to explore the effects of LAM and LLI on capacity fade in cyclic ageing tests. It is predicted that the loss of cyclable lithium (trapped in the degraded shell) leads to a shift in the stoichiometry range of the negative electrode but does not directly contribute to the capacity loss, and that the loss of positive electrode active materials dominates the fade of usable cell capacity in discharge. The available capacity at a given current rate is further decreased by the additional resistance of the degraded shell layer. The change pattern of the state-of-charge curve provides information of more dimensions than the conventional capacity-fade curve, beneficial to the diagnosis of degradation modes. The model has been implemented into PyBaMM and made available as open source codes.