Microwave magnetic excitations in U-type hexaferrite Sr$_4$CoZnFe$_{36}$O$_{60}$ ceramics

Abstract

Microwave (MW) transmission, absorption, and reflection loss spectra of the ferrimagnetic U-type hexaferrite Sr$_4$CoZnFe$_{36}$O$_{60}$ ceramics were studied from 100 MHz to 35 GHz at temperatures between 10 and 390 K. 9 MW magnetic excitations with anomalous behavior near the ferrimagnetic phase transitions were revealed. They also change under the application of weak bias magnetic field (0 - 700 Oe) at room temperature. 6 pure magnetic modes are assigned to dynamics of the magnetic domain walls and inhomogeneous magnetic structure of the ceramics, to the natural ferromagnetic resonance (FMR) and to the higher-frequency magnons. Three modes are considered as the magnetodielectric ones with dominating influence of the magnetic properties on their temperature and field dependences. Presence of the natural FMR in all ferrimagnetic phases proves existence of the non-zero internal magnetization and magnetocrystalline anisotropy. Splitting of the FMR into the two components without magnetic bias was observed in the collinear phase and is attributed to a change of the magnetocrystalline anisotropy during the phase transition. The high-frequency FMR component critically slows down to the phase transition. At room temperature, the FMR splitting and essential suppression of the higher-frequency modes was revealed under the weak bias field (300 - 700 Oe). The highly nonlinear MW response and the FMR splitting are caused by the gradual evolution of the polydomain magnetic structure to a monodomain one. The high number of magnetic excitations observed in the MW region confirms the suitability of using hexaferrite Sr$_4$CoZnFe$_{36}$O$_{60}$ ceramics as MW absorbers, shielding materials and highly tunable filters.