Influence of the pretreatment anneal on Co germanide Schottky contacts

Abstract

A thin cobalt layer is deposited by electron beam evaporation onto a germanium substrate after an in situ cleaning annealing at 400 or 700 C. The effect of these pretreatments on the Co/Ge Schottky barrier properties and on the germanide formation is investigated by using different techniques. A strong influence of the pre-treatment is observed. The pre-treatment at 700 C removes the native oxide but enhances the diffusion of contaminants. After post-metal deposition annealing, the sample pre-treated at 700 C shows a double layer structure due to interdiffusion, whereas some large isolated islands are present in the sample pre-treated at 400 C.