Step bunching during Si(001) homoepitaxy caused by the surface diffusion anisotropy
J. Myslivecek, C. Schelling, F. Schaffler, G. Springholz, P. Smilauer, J. Krug, B. Voigtlander
Abstract
Scanning tunneling microscopy experiments show that the unstable growth morphology observed during molecular beam homoepitaxy on slightly vicinal Si(001) surfaces consists of straight step bunches. The instability occurs under step- flow growth conditions and vanishes both during low-temperature island growth and at high temperatures. An instability with the same characteristics is observed in a 2D Kinetic Monte Carlo model of growth with incorporated Si(001)- like diffusion anisotropy. This provides strong evidence that the diffusion anisotropy destabilizes growth on Si(001) and similar surfaces towards step bunching. This new instability mechanism is operational without any additional step edge barriers.
Create a lesson
Related papers
A Gaussian process coarse-grained potential for Na-montmorillonite
Yalda Pedram, Yaoting Zhang, Laurent Brochard et al.
First-principles theory of phonon renormalization from nonlinear electron-phonon interactions
Florian Kluibenschedl, Matthew Houtput, Jacques Tempere et al.
Spin-Lattice Dynamics and Interactions in Magnonic Spinels
Hari Paudyal, Yuri Suzuki, Michael E. Flatté et al.
Magnon-Phonon Dynamics in Multidimensional Antiferromagnetic Oxides
Yogendra Limbu, Michael E. Flatté, Durga Paudyal
Strain-Induced Metal-to-Insulator Transition in Antiferromagnetic SrCrO3 Thin Films
S. Jöhr, A. Carta, J. Moreno et al.
Tuning the Coercive Field in Ferroelectric Hf0.5Zr0.5O2-Al2O3 Heterostructures via Interfacial Charge Dynamics
Marshall B. Frye, Chanyoung Kim, Jeong-Woo Sun et al.