Interface-Confined Superconductivity with Thickness-Independent Superfluid Stiffness in (Pb,Sn)Te/FeTe Bilayers

Abstract

Interface-induced superconductivity in FeTe-based heterostructures provides a promising route toward topological superconductivity, yet the roles of the neighboring layers topology, symmetry, and electronic structure remain unresolved. In this work, we employ molecular beam epitaxy to grow Pb1-xSnxTe/FeTe bilayers and use angle-resolved photoemission spectroscopy to track the evolution of the Pb1-xSnxTe layer from a trivial insulator to a topological crystalline insulator hosting multiple Dirac surface states. Electrical transport measurements reveal robust superconductivity throughout the entire composition range, with a nearly constant superconducting transition temperature of ~12 K despite substantial changes in the electronic structure and topology of Pb1-xSnxTe. Double-coil mutual-inductance measurements further reveal comparable superfluid stiffness across the topological phase transition and nearly thickness-independent superfluid stiffness despite large variations in the constituent-layer thicknesses, demonstrating that superconductivity is confined near the interface. These results establish that superconductivity in FeTe-based heterostructures is largely insensitive to the topology, crystal symmetry, and detailed electronic structure of the neighboring layer, supporting a primary origin in modifications to the FeTe layer. The coexistence of interface-confined superconductivity and tunable multiple Dirac surface states in Pb1-xSnxTe/FeTe bilayers provides a versatile platform for exploring topological superconductivity and interactions among multiple Majorana zero modes.