Superconducting MgB(2) films via precursor post-processing approach
M. Paranthaman, C. Cantoni, H. Y. Zhai, H. M. Christen, T. Aytug, S. Sathyamurthy, E. D. Specht, J. R. Thompson, D. H. Lowndes, H. R. Kerchner, D. K. Christen
Abstract
Superconducting MgB(2) films with Tc = 38.6 K were prepared using a precursor-deposition, ex-situ post-processing approach. Precursor films of boron, ~0.5 micrometer thick, were deposited onto Al(2)O(3) (102) substrates by e-beam evaporation; a post-anneal at 890 deg C in the presence of bulk MgB(2) and Mg metal produced highly crystalline MgB(2) films. X-ray diffraction indicated that the films exhibit some degree of c-axis alignment, but are randomly oriented in-plane. Transport current measurements of the superconducting properties show high values of the critical current density and yield an irreversibility line that exceeds that determined by magnetic measurements on bulk polycrystalline materials.
Create a lesson
Related papers
Superconductivity in Pb2-xBixPd Single Crystals
S. Srivastava, R. P. Singh
Type-I superconductivity in a quasi-2D topologically nontrivial YbBi2
Karolina Górnicka, Sudip Malick, Joanna Bławat et al.
Generic thermodynamics of condensates with extremely small superfluid density ---Application to UTe2 and hidden second phase transition---
Kazushige Machida
Vortex-mediated spin current injection into two-dimensional superconductor NbSe2
Meng Yang, Xiaolong Yin, Jingjing Liu et al.
Superconductivity at the metal-insulator phase boundary in a bulk nickelate at ambient pressure
Hyo-Bin Ahn, Xinglong Chen, Hong Zheng et al.
Crystallographic imperfections and exotic superconductivity of UBe13
Andreas Leithe-Jasper, Markus König, Yusei Shimizu et al.