A Cross-Whiskers Junction as a Novel Fabrication Process for Intrinsic Josephson Junction
Yoshihiko Takano, Takeshi Hatano, Akihiro Fukuyo, Akira Ishii, Shunichi Arisawa, Masashi Tachiki, Kazumasa Togano
Abstract
A Bi2Sr2CaCu2O8+d cross-whiskers junction has been successfully discovered as a novel intrinsic Josephson junction without using any technique for micro-fabrication. Two Bi2Sr2CaCu2O8+d whisker crystals were placed crosswise on a MgO substrate and heated at 850C for 30 min. They were electrically connected at their c-planes. The measurement terminals were made at the four ends of the whiskers. The I-V characteristics of the cross-whiskers junction at 5K were found to show a clear multiple-branch structure with a spacing of approximately 15 mV that is a feature of the intrinsic Josephson junction. The critical current density Jc was estimated to be 1170 A/cm2. The branch-structure was strongly suppressed by the magnetic field above 1kOe.
Create a lesson
Related papers
Ta-based S-I-S junctions for integrated superconducting Electronics
Trent Borman, Cameron Bullock, Cole Chason et al.
Nonreciprocal charge transport in quantum materials: From superconductors to magnetic systems
Boning Yu, Yalei Huang, Alltrin Dhanarajagopal et al.
Intra-unit-cell Josephson scanning tunneling spectroscopy of the cuprate Bi1.2Pb0.8Sr2CaCu2O8+δ
Fengyu Yao, Jiong Mei, Wenjin Mao et al.
Constraining the Superconducting Gap of Monolayer FeSe/SrTiO3 via Statistical Analysis and Tip-Height-Dependent Tunneling Spectroscopy
Dongwon Shin, Xiyou Peng, Kaleb McClure et al.
Acoustic damping limits superfluid helium as a thermal bath for mechanical resonators
Yunhu Huang, Mehri Ebrahimi, Alireza Rashedi et al.
Superinsulation, electric confinement in condensed matter
M. Cristina Diamantini, Carlo A. Trugenberger