Effects of Pressure on Electron Transport and Local Structure of Manganites: Low to High Pressure Regime
Congwu Cui, Trevor A. Tyson, Zhong Zhong, Jeremy P. Carlo, Yuhai Qin
Abstract
The pressure dependence of the resistivity and structure of La0.60Y0.07Ca0.33MnO3 has been explored in the pressure range from 1 atm to ~7 GPa. The metal to insulator transition temperature (TMI) was found to reach a maximum and the resistivity achieves a minimum at ~3.8 GPa. Beyond this pressure, TMI is reduced with a concomitant increase in the resistivity. Structural measurements at room temperature show that at low pressure (below 2 GPa) the Mn-O bond lengths are compressed. Between ~2 and ~4 GPa, a pressure induced enhancement of the Jahn-Teller (JT) distortion occurs in parallel with an increase in Mn-O1-Mn bond angle to ~180 (degree). Above ~4 GPa, the Mn-O1-Mn bond angle is reduced while the JT distortion appears to remain unchanged. The resistivity above TMI is well modeled by variable range hopping. The pressure dependence of the localization length follows the behavior of TMI.
Create a lesson
Related papers
A Gaussian process coarse-grained potential for Na-montmorillonite
Yalda Pedram, Yaoting Zhang, Laurent Brochard et al.
First-principles theory of phonon renormalization from nonlinear electron-phonon interactions
Florian Kluibenschedl, Matthew Houtput, Jacques Tempere et al.
Spin-Lattice Dynamics and Interactions in Magnonic Spinels
Hari Paudyal, Yuri Suzuki, Michael E. Flatté et al.
Magnon-Phonon Dynamics in Multidimensional Antiferromagnetic Oxides
Yogendra Limbu, Michael E. Flatté, Durga Paudyal
Strain-Induced Metal-to-Insulator Transition in Antiferromagnetic SrCrO3 Thin Films
S. Jöhr, A. Carta, J. Moreno et al.
Tuning the Coercive Field in Ferroelectric Hf0.5Zr0.5O2-Al2O3 Heterostructures via Interfacial Charge Dynamics
Marshall B. Frye, Chanyoung Kim, Jeong-Woo Sun et al.