Superconductivity of MI(MII0.5, Si0.5)2 (MI=Sr and Ba, MII=Al and Ga), ternary silicides with the AlB2-type structure
Motoharu Imai, Kenji Nishida, Takashi Kimura, Hideaki Kitazawa, Hideki Abe, Hijiri Kito, Kenji Yoshii
Abstract
Ternary silicides MI(MII0.5, Si0.5)2 (MI=Sr and Ba, MII=Al and Ga) were prepared by Ar arc melting. Powder X-ray diffraction indicates that they have the AlB2-type structure, in which Si and MII atoms are arranged in honeycomb layers and MI atoms are intercalated between them. Electrical resistivity and dc magnetization measurements revealed that Sr(Al0.5, Si0.5)2 is superconductive, with a critical temperature for superconductivity (TC) of 4.2 K, while Ba(Al0.5, Si0.5)2 is not at temperatures ranging above 2.0 K. Sr(Ga0.5, Si0.5)2 and Ba(Ga0.5, Si0.5)2 are also superconductors, with TCs of 5.1 and 3.3 K, respectively.
Create a lesson
Related papers
Superconductivity in Pb2-xBixPd Single Crystals
S. Srivastava, R. P. Singh
Type-I superconductivity in a quasi-2D topologically nontrivial YbBi2
Karolina Górnicka, Sudip Malick, Joanna Bławat et al.
Generic thermodynamics of condensates with extremely small superfluid density ---Application to UTe2 and hidden second phase transition---
Kazushige Machida
Vortex-mediated spin current injection into two-dimensional superconductor NbSe2
Meng Yang, Xiaolong Yin, Jingjing Liu et al.
Superconductivity at the metal-insulator phase boundary in a bulk nickelate at ambient pressure
Hyo-Bin Ahn, Xinglong Chen, Hong Zheng et al.
Crystallographic imperfections and exotic superconductivity of UBe13
Andreas Leithe-Jasper, Markus König, Yusei Shimizu et al.