Formation and mobility of oxygen vacancies in RuSr2GdCu2O8
F. Cordero, M. Ferretti, M. R. Cimberle, R. Masini
Abstract
Oxygen vacancies are introduced in the RuO2 and possibly CuO2 planes of RuSr2GdCu2O8 by annealing in vacuum above 600 K. The diffusive jumps of the O vacancies are accompanied by a reorientation of the local distortion, and are probed by measuring the elastic energy loss and modulus versus temperature at 1-10 kHz. An intense acoustic absorption peak develops near 670 K at 1 kHz and finally stabilizes after heating up to 920 K in vacuum. The analysis of the peak shows a barrier for the O diffusion of ~1.4 eV, and a slowing down of Curie-Weiss type, with Tc = 400-470 K, due to the interaction among the O vacancies. A secondary peak is attributed to O vacancies trapped at defects in the RuO2 planes, or to vacancies in the CuO2 planes. No sign of structural phase transformation is found up to 920 K.
Create a lesson
Related papers
Superconductivity in Pb2-xBixPd Single Crystals
S. Srivastava, R. P. Singh
Type-I superconductivity in a quasi-2D topologically nontrivial YbBi2
Karolina Górnicka, Sudip Malick, Joanna Bławat et al.
Generic thermodynamics of condensates with extremely small superfluid density ---Application to UTe2 and hidden second phase transition---
Kazushige Machida
Vortex-mediated spin current injection into two-dimensional superconductor NbSe2
Meng Yang, Xiaolong Yin, Jingjing Liu et al.
Superconductivity at the metal-insulator phase boundary in a bulk nickelate at ambient pressure
Hyo-Bin Ahn, Xinglong Chen, Hong Zheng et al.
Crystallographic imperfections and exotic superconductivity of UBe13
Andreas Leithe-Jasper, Markus König, Yusei Shimizu et al.