Training of the Ni-Mn-Fe-Ga ferromagnetic shape-memory alloys by cycling in a high magnetic field
A. A. Cherechukin, V. V. Khovailo, R. V. Koposov, E. P. Krasnoperov, T. Takagi, J. Tani
Abstract
The temperature and magnetic field dependencies of Ni-Mn-Ga polycrystals deformation are investigated. Ingots were prepared by arc-melting in argon atmosphere and further annealing. A training procedure (cycling across the martensitic transition point) for the two-way shape-memory effect was performed with Ni2.16Fe0.04Mn0.80Ga samples. Changes in sample deformations were noticed with changing the magnetic field at a constant temperature. The first cycle deformation increment as compared with the initial value (in the austenitic state at zero field) in the course of the martensitic transition was 0.29%, and 0.41% and 0.48% for the second and third cycles, respectively.
Create a lesson
Related papers
A Gaussian process coarse-grained potential for Na-montmorillonite
Yalda Pedram, Yaoting Zhang, Laurent Brochard et al.
First-principles theory of phonon renormalization from nonlinear electron-phonon interactions
Florian Kluibenschedl, Matthew Houtput, Jacques Tempere et al.
Spin-Lattice Dynamics and Interactions in Magnonic Spinels
Hari Paudyal, Yuri Suzuki, Michael E. Flatté et al.
Magnon-Phonon Dynamics in Multidimensional Antiferromagnetic Oxides
Yogendra Limbu, Michael E. Flatté, Durga Paudyal
Strain-Induced Metal-to-Insulator Transition in Antiferromagnetic SrCrO3 Thin Films
S. Jöhr, A. Carta, J. Moreno et al.
Tuning the Coercive Field in Ferroelectric Hf0.5Zr0.5O2-Al2O3 Heterostructures via Interfacial Charge Dynamics
Marshall B. Frye, Chanyoung Kim, Jeong-Woo Sun et al.