Evolution of In-Plane Magnetic Anisotropy In Sputtered FeTaN/TaN/FeTaN Sandwich Films
H. B. Nie, C. K. Ong, J. P. Wang, Z. W. Li
Abstract
FeTaN/TaN/FeTaN sandwich films, FeTaN/TaN and TaN/FeTaN bilayers were synthesized by using RF magnetron sputtering. The magnetic properties, crystalline structures, microstructures and surface morphologies of the as-deposited samples were characterized using angle-resolved M-H loop tracer, VSM, XRD, TEM, AES and AFM. An evolution of the in-plane anisotropy was observed with the changing thickness of the nonmagnetic TaN interlayer in the FeTaN/TaN/FeTaN sandwiches, such as the easy-hard axis switching and the appearing of biaxial anisotropy. It is ascribed to three possible mechanisms, which are interlayer magnetic coupling, stress, and interface roughness, respectively. Interlayer coupling and stress anisotropies may be the major reasons to cause the easy-hard axis switching in the sandwiches. Whereas, magnetostatic and interface anisotropies may be the major reasons to cause biaxial anisotropy in the sandwiches, in which magnetostatic anisotropy is the dominant one.
Create a lesson
Related papers
Necessary conditions for benchmarking next-generation AI in materials discovery
Daniel E Widdowson, Tatiana V Kurlina, Olga D Anosova et al.
Doubly Metastable Synthesis for Accelerated Quantum Materials Discovery
Kyuho Lee, Berit H. Goodge, Soonhyun Kwon et al.
Phononic Frequency Combs in Twisted Bilayer Transition Metal Dichalcogenide Heterostructures from First Principles
Naman Arora, Adarsh Ganesan
Improved screening of doped ZrO2 catalysts for CO2 hydrogenation from graph-based machine learning
Karsten Walz Jensen, Mie Andersen, Raffaele Cheula
Dislocation mediated twin boundary faceting in β-Sn
John Israel, Ian Chesser, Khanh Dang et al.
Ferroelectric Domain-Wall Motion, Stability, and Frequency Responses under Different Screening-Charge Conservation Laws
Sergei V. Kalinin