Preparation, characterization and magnetic studies of Bi0.5 X0.5(X=Ca,Sr)MnO3 nanoparticles
S S Rao, S V Bhat
Abstract
Nanoparticles (dia ~ 5 - 7 nm) of Bi0.5 X0.5(X=Ca,Sr)MnO3 are prepared by polymer assisted sol-gel method and characterized by various physico-chemical techniques. X-ray diffraction gives evidence for single phasic nature of the materials as well as their structures. Mono dispersed to a large extent, isolated nanoparticles are seen in the transmission electron micrographs. High resolution electron microscopy shows the crystalline nature of the nanoparticles. Superconducting quantum interferometer based magnetic measurements from 10 K to 300 K show that these nanomanganites retain the charge ordering (CO) nature unlike Pr and Nd based nanomanganites. The CO in Bi based manganites is thus found to be very robust consistent with the observation that magnetic field of the order of 130 T are necessary to melt the CO in these compounds. These results are supported by electron magnetic resonance measurements.
Create a lesson
Related papers
Metallogenic quantum criticality: Fermi surface nucleation at transitions between gapped phases
Zhengyan Darius Shi
Exact Stiffness and Dynamical Responses from Fock-Space Fragmentation
Jonah Herzog-Arbeitman, Eslam Khalaf, Zhaoyu Han
A continuous confinement-deconfinement transition in a triangular quantum magnet
Suguru Hosoi, Sejun Park, Michihiro Hirata et al.
Multi-orbital physics in inverse Lieb lattice altermagnets
Mercè Roig, Jannik Gondolf, Andreas Kreisel et al.
3D- (H-theta-phi) magnetic phase diagram of antiferromagnetic metal GdB6 with electron and lattice instability
A. N. Azarevich, A. V. Bogach, T. F. Garipova et al.
Interlayer-engineering of Charge Order Wave Vector in Kagome Metals
Muntafa M. Mahi, Quazi D. M. Khosru, M. Zahid Hasan et al.