Synthesis and Magnetic Properties of Cobalt Ferrite (CoFe2O4) Nanoparticles Prepared by Wet Chemical Route
K. Maaz, Arif Mumtaz, S. K. Hasanain, Abdullah Ceylan
Abstract
Magnetic nanoparticles of cobalt ferrite have been synthesized by wet chemical method using stable ferric and cobalt salts with oleic acid as the surfactant. X-ray Diffraction (XRD) and Transmission Electron Microscope (TEM) confirmed the formation of single phase cobalt ferrite nanoparticles in the range 15-48nm depending on the annealing temperature and time. The size of the particles increases with annealing temperature and time while the coercivity goes through a maximum, peaking at around 28nm. A very large coercivity (10.5kOe) is observed on cooling down to 77K while typical blocking effects are observed below about 260K. The high field moment is observed to be small for smaller particles and approaches the bulk value for large particles.
Create a lesson
Related papers
Temperature dependence of the charge density from first principles: application to the (222) forbidden reflection in silicon
Jean Paul Nery, Raveena Gupta, Olle Hellman et al.
Coupled anisotropic weak topological states and Floquet mixed-parity altermagnetism in two-dimensional Su-Schrieffer-Heeger models
Kunyuan Feng, Xibin Liu, Chenchen Liu et al.
Grain Boundary Phase Transitions Enable Diffusionless Climb of Disconnections
Md Sharier Nazim, Giacomo Po, Nikhil Chandra Admal
3D Cloud Component Analysis of Atomic Structures
Pai Li
Benchmarking of Fast and Interpretable UF Machine Learning Potentials
Pawan Prakash, Sam Dong, Richard G. Hennig
Grain-Boundary Premelting in High-Entropy Transition Metal Carbides
Marium M. Mou, Caleb Schenck, Samuel E. Daigle et al.