X. Marti, F. Sanchez, D. Hrabovsky, L. Fabrega, A. Ruyter, J. Fontcuberta, V. Laukhin, V. Skumryev, M. V. Garcia-Cuenca, C. Ferrater, M. Varela, A. Vila, U. Luders, J. F. Bobo
Abstract
We report on the growth and functional characterization of epitaxial thin films of the multiferroic YMnO3. We show that using Pt as a seed layer on SrTiO3(111) substrates, epitaxial YMnO3 films (0001) textured are obtained. An atomic force microscope has been used to polarize electric domains revealing the ferroelectric nature of the film. When a Permalloy layer is grown on top of the YMnO3(0001) film, clear indications of exchange bias and enhanced coercivity are observed at low temperature. The observation of coexisting antiferromagnetism and electrical polarization suggests that the biferroic character of YMnO3 can be exploited in novel devices.
Create a lesson
Related papers
Metallogenic quantum criticality: Fermi surface nucleation at transitions between gapped phases
Zhengyan Darius Shi
Exact Stiffness and Dynamical Responses from Fock-Space Fragmentation
Jonah Herzog-Arbeitman, Eslam Khalaf, Zhaoyu Han
A continuous confinement-deconfinement transition in a triangular quantum magnet
Suguru Hosoi, Sejun Park, Michihiro Hirata et al.
Multi-orbital physics in inverse Lieb lattice altermagnets
Mercè Roig, Jannik Gondolf, Andreas Kreisel et al.
3D- (H-theta-phi) magnetic phase diagram of antiferromagnetic metal GdB6 with electron and lattice instability
A. N. Azarevich, A. V. Bogach, T. F. Garipova et al.
Interlayer-engineering of Charge Order Wave Vector in Kagome Metals
Muntafa M. Mahi, Quazi D. M. Khosru, M. Zahid Hasan et al.