Strain induced pressure effect in pulsed laser deposited thin films of the strongly correlated oxide V2O3
S. Autier-Laurent, B. Mercey, D. Chippaux, P. Limelette, Ch. Simon
Abstract
V2O3 thin films about 10 nm thick were grown on Al2O3 (0001) by pulsed laser deposition. The XRD analysis is in agreement with R-3c space group. Some of them exhibit the metal / insulator transition characteristic of V2O3 bulk material and others samples exhibit a metallic behavior. For the latter, the XPS analysis indicates an oxidation state of +III for vanadium. There is no metal / insulator transition around 150 K in this sample and a strongly correlated Fermi liquid rho = AT2 behavior of the resistivity at low temperature is observed, with a value of A of 1.2 10-4 ohm cm, 3 times larger than the bulk value at 25 kbar.
Create a lesson
Related papers
Metallogenic quantum criticality: Fermi surface nucleation at transitions between gapped phases
Zhengyan Darius Shi
Exact Stiffness and Dynamical Responses from Fock-Space Fragmentation
Jonah Herzog-Arbeitman, Eslam Khalaf, Zhaoyu Han
A continuous confinement-deconfinement transition in a triangular quantum magnet
Suguru Hosoi, Sejun Park, Michihiro Hirata et al.
Multi-orbital physics in inverse Lieb lattice altermagnets
Mercè Roig, Jannik Gondolf, Andreas Kreisel et al.
3D- (H-theta-phi) magnetic phase diagram of antiferromagnetic metal GdB6 with electron and lattice instability
A. N. Azarevich, A. V. Bogach, T. F. Garipova et al.
Interlayer-engineering of Charge Order Wave Vector in Kagome Metals
Muntafa M. Mahi, Quazi D. M. Khosru, M. Zahid Hasan et al.