Swift-heavy-ion-irradiation-induced enhancement in electrical conductivity of chemical solution deposited La0.7Ba0.3MnO3 thin films
R. N. Parmar, J. H. Markna, D. G. Kuberkar, Ravi Kumar, D. S. Rana, Vivas C. Bagve, S. K. Malik
Abstract
Epitaxial thin films of La0.7Ba0.3MnO3 manganite, deposited using Chemical Solution Deposition technique, were irradiated by 200 MeV Ag+15 ions with a maximum ion dose up to 1x1012 ions/cm2. Temperature- and magnetic field-dependent resistivity measurements on all the films (before and after irradiation) reveal a sustained decrease in resistivity with increasing ion dose. A maximum dose of 1x1012 ions/cm2 suppresses resistivity by factors of 3 and 10, at 330 K [insulator-metal (I-M) transition] and at 10 K, respectively. On the other hand, with increasing ion dose, the magnetoresistance (MR) enhances in the vicinity of I-M transition but decreases at low temperatures. These results, corroborated by surface morphology of films, suggest that the origin of such properties lies in the irradiation induced improved crystallinity and epitaxial orientation, enhanced connectivity between grains, and conglomeration of grains which result in better conductivity at grain boundaries.
Create a lesson
Related papers
Temperature dependence of the charge density from first principles: application to the (222) forbidden reflection in silicon
Jean Paul Nery, Raveena Gupta, Olle Hellman et al.
Coupled anisotropic weak topological states and Floquet mixed-parity altermagnetism in two-dimensional Su-Schrieffer-Heeger models
Kunyuan Feng, Xibin Liu, Chenchen Liu et al.
Grain Boundary Phase Transitions Enable Diffusionless Climb of Disconnections
Md Sharier Nazim, Giacomo Po, Nikhil Chandra Admal
3D Cloud Component Analysis of Atomic Structures
Pai Li
Benchmarking of Fast and Interpretable UF Machine Learning Potentials
Pawan Prakash, Sam Dong, Richard G. Hennig
Grain-Boundary Premelting in High-Entropy Transition Metal Carbides
Marium M. Mou, Caleb Schenck, Samuel E. Daigle et al.