Nanomechanics of Advanced Polymer Fibres
Philippe Colomban
Abstract
The micro/nano-structural evolution before and after tensile/compressive loading, fatigue and ultimately, failure has been studied by Raman (and IR) microspectroscopy for PBO, PET, PA66, PP, silk and hair using three probes: low wavenumber collective modes at <150cm-1 as representative of the crystalline/ordered and amorphous chains, stretching and bending modes, as representative of the C-C/ C-N polymeric backbone, and localized vibrations (OH, NH) to probe the inter-macromolecule segment distance. Wavenumber and bandwidth distribution across fibre diameters reveal different types of skin/core heterogeneity. The in situ analysis at different strain/pressure levels shows that amorphous chains in the fibre accommodate the stress differently. The post mortem analysis shows that amorphous domains can be higly stressed during the failure and remnant stress can be measured.
Create a lesson
Related papers
Temperature dependence of the charge density from first principles: application to the (222) forbidden reflection in silicon
Jean Paul Nery, Raveena Gupta, Olle Hellman et al.
Coupled anisotropic weak topological states and Floquet mixed-parity altermagnetism in two-dimensional Su-Schrieffer-Heeger models
Kunyuan Feng, Xibin Liu, Chenchen Liu et al.
Grain Boundary Phase Transitions Enable Diffusionless Climb of Disconnections
Md Sharier Nazim, Giacomo Po, Nikhil Chandra Admal
3D Cloud Component Analysis of Atomic Structures
Pai Li
Benchmarking of Fast and Interpretable UF Machine Learning Potentials
Pawan Prakash, Sam Dong, Richard G. Hennig
Grain-Boundary Premelting in High-Entropy Transition Metal Carbides
Marium M. Mou, Caleb Schenck, Samuel E. Daigle et al.