Characterization of transport and magnetic properties in thin film La(0.67)(Ca(x)Sr(1-x))(0.33)MnO(3) mixtures
P. R. Broussard, S. B. Qadri, V. M. Browning, V. C. Cestone
Abstract
We have grown thin films of (100) oriented La0.67(CaxSr1-x)0.33MnO3 on (100) NdGaO3 substrates by off-axis sputtering. We have looked at the changes in the resistivity and magnetoresistance of the samples as the Ca/Sr ratio was varied. We find that as the calcium fraction is decreased, the lattice match to the substrate decreases, and the films become more disordered, as observed in transport measurements and the variation in Curie and peak resistance temperatures. We find a correlation between the temperature independent and T2 terms to the low temperature resistivity. The room temperature magnetoresistance exhibits a maximum as the peak temperature is increased by the substitution of Sr for Ca, and a change in the field dependence to the resistivity at room temperature is observed.
Create a lesson
Related papers
Metallogenic quantum criticality: Fermi surface nucleation at transitions between gapped phases
Zhengyan Darius Shi
Exact Stiffness and Dynamical Responses from Fock-Space Fragmentation
Jonah Herzog-Arbeitman, Eslam Khalaf, Zhaoyu Han
A continuous confinement-deconfinement transition in a triangular quantum magnet
Suguru Hosoi, Sejun Park, Michihiro Hirata et al.
Multi-orbital physics in inverse Lieb lattice altermagnets
Mercè Roig, Jannik Gondolf, Andreas Kreisel et al.
3D- (H-theta-phi) magnetic phase diagram of antiferromagnetic metal GdB6 with electron and lattice instability
A. N. Azarevich, A. V. Bogach, T. F. Garipova et al.
Interlayer-engineering of Charge Order Wave Vector in Kagome Metals
Muntafa M. Mahi, Quazi D. M. Khosru, M. Zahid Hasan et al.