A tetragonal-to-monoclinic phase transition in a ferroelectric perovskite: the structure of PbZr(0.52)Ti(0.48)O3
B. Noheda, J. A. Gonzalo, L. E. Cross, R. Guo, S-E. Park, D. E. Cox, G. Shirane
Abstract
The perovskite-like ferroelectric system PbZr(1-x)Ti(x)O3 (PZT) has a nearly vertical morphotropic phase boundary (MPB) around x=0.45-0.50. Recent synchrotron x-ray powder diffraction measurements by Noheda et al. [Appl. Phys. Lett. 74, 2059 (1999)] have revealed a new monoclinic phase between the previously-established tetragonal and rhombohedral regions. In the present work we describe a Rietveld analysis of the detailed structure of the tetragonal and monoclinic PZT phases on a sample with x= 0.48 for which the lattice parameters are respectively: at= 4.044 A, ct= 4.138 A, at 325 K, and am= 5.721 A, bm= 5.708 A, cm= 4.138 A, beta= 90.496 deg., at 20K. In the tetragonal phase the shifts of the atoms along the polar [001] direction are similar to those in PbTiO3 but the refinement indicates that there are, in addition, local disordered shifts of the Pb atoms of ~0.2 A perpendicular to the polar axis.. The monoclinic structure can be viewed as a condensation along one of the <110> directions of the local displacements present in the tetragonal phase. It equally well corresponds to a freezing-out of the local displacements along one of the <100> directions recently reported by Corker et al.[J. Phys. Condens. Matter 10, 6251 (1998)] for rhombohedral PZT. The monoclinic structure therefore provides a microscopic picture of the MPB region in which one of the "locally" monoclinic phases in the "average" rhombohedral or tetragonal structures freezes out, and thus represents a bridge between these two phases.
Create a lesson
Related papers
Temperature dependence of the charge density from first principles: application to the (222) forbidden reflection in silicon
Jean Paul Nery, Raveena Gupta, Olle Hellman et al.
Coupled anisotropic weak topological states and Floquet mixed-parity altermagnetism in two-dimensional Su-Schrieffer-Heeger models
Kunyuan Feng, Xibin Liu, Chenchen Liu et al.
Grain Boundary Phase Transitions Enable Diffusionless Climb of Disconnections
Md Sharier Nazim, Giacomo Po, Nikhil Chandra Admal
3D Cloud Component Analysis of Atomic Structures
Pai Li
Benchmarking of Fast and Interpretable UF Machine Learning Potentials
Pawan Prakash, Sam Dong, Richard G. Hennig
Grain-Boundary Premelting in High-Entropy Transition Metal Carbides
Marium M. Mou, Caleb Schenck, Samuel E. Daigle et al.