A New Direct Process to Prepare YBa2Cu3O7- films on Biaxially Textured Ag110<211>
Rongping Wang, Yueliang Zhou, Shaohua Pan, Meng He, Zhenghao Chen, Guozhen Yang
Abstract
YBCO films were successfully prepared on biaxially textured Ag110<211> substrates by using pulsed laser deposition. X-ray diffraction results showed that the degree of preferential orientation of Ag110<211> substrates varied with increasing annealing temperature. With a thin template layer deposited at low temperature, YBCO film with c-axis orientation and in-plane biaxial alignment could be obtained at high deposition temperature. Scanning electron microscopy observation revealed that YBCO grains enlarged but Ag grains on the surface of the YBCO films became smaller with increasing deposition temperature. At optimal deposition conditions, Ag atoms diffuse into the YBCO grain boundaries, and then fill in the weak-link regions in the YBCO film, resulting in the conduction easier. Jc value of 5105A/cm2 was obtained at 77K and zero magnetic field for the best YBCO film in our work.
Create a lesson
Related papers
Temperature dependence of the charge density from first principles: application to the (222) forbidden reflection in silicon
Jean Paul Nery, Raveena Gupta, Olle Hellman et al.
Coupled anisotropic weak topological states and Floquet mixed-parity altermagnetism in two-dimensional Su-Schrieffer-Heeger models
Kunyuan Feng, Xibin Liu, Chenchen Liu et al.
Grain Boundary Phase Transitions Enable Diffusionless Climb of Disconnections
Md Sharier Nazim, Giacomo Po, Nikhil Chandra Admal
3D Cloud Component Analysis of Atomic Structures
Pai Li
Benchmarking of Fast and Interpretable UF Machine Learning Potentials
Pawan Prakash, Sam Dong, Richard G. Hennig
Grain-Boundary Premelting in High-Entropy Transition Metal Carbides
Marium M. Mou, Caleb Schenck, Samuel E. Daigle et al.