Resistivity and Magneto-Optical Evidence for Variable and Incomplete Connectivity in Dense, High Critical Current Density C-alloyed Magnesium Diboride
B. J. Senkowicz, A. A. Polyanskii, R. J. Mungall, E. E. Hellstrom, D. C. Larbalestier
Abstract
Carbon-doped magnesium diboride was fabricated from pre-reacted pure MgB2 by mechanical alloying. The sample set had excellent critical current densities Jc(8T,4.2K) ranging from 15-60 kA/cm2, depending on composition. Magneto-optical imaging detected regions up to 0.5 mm in size which were nearly 100% dense with Jc 2-6 times that of the matrix. Evaluation of resistivity curves using the Rowell method predicts that only 10-50% of the cross sectional area carries the normal state measurement current, suggesting that considerable increases in Jc in these ~80% dense MgB2 samples would be possible with complete grain and particle connectivity.
Create a lesson
Related papers
High-Temperature Superconductivity of the Fe-Se-H compound
S. I. Bondarenko, A. A. Prokhorov, N. N. Galtsov et al.
Stabilization of Interband Phase Solitons in Two-Band Noncentrosymmetric Superconducting Rings
Yuriy Yerin, Boris Malomed, Stefan-Ludwig Drechsler et al.
Strain-driven orbital-selective reconstruction and bicollinear-to-stripe evolution in FeTe
Zhenfeng Ouyang, Yin Chen, Yi-Heng Tian et al.
Supercurrent detection and manipulation of topological phase transitions in Shiba-Majorana hybrid systems
Debika Debnath, Ioannis Ioannidis, Paramita Dutta et al.
Exact pair density wave in topological moire flat bands and universal superfluid stiffness
Zhengzhi Wu, Ming-rui Li, Hong Yao
Electrical manipulation of oxygen stoichiometry in multiterminal YBa2Cu3O7-δ junctions
Daniel Stoffels, Caio C. Quaglio-Gomes, Nicolas Lejeune et al.