Discovery of Li2(Pd,Pt)3B superconductors
P. Badica, K. Togano, H. Takeya, K. Hirata, S. Awaji, K. Watanabe
Abstract
Critical temperature Tc of the Li2(Pd1-xPtx)3B was reported to be 7-8K for x=0 and 2.2-2.8K for x=1. In this article we present our preliminary results on behavior of magnetization-temperature curves with starting composition of Pd-B precursor, y-Li concentration in LiyPd3B and post-annealing of the Pd-end compound. Results suggest that to maximize Tc ratio Pd:B should be close to 3:1, while y-Li has to be optimum. The lowest Tc for LiyPd3B was 4.4-4.6K, while post-annealings at 560 deg. C allowed enhancement of Tc up to 8.2-8.4K. Compositions Li2Z3B with Z=Ni, Ru, Rh, Re, Ag are not superconducting down to 1.8K. Exception is composition with Re showing superconductivity due to Re3B compound. All samples were prepared by arc melting.
Create a lesson
Related papers
High-Temperature Superconductivity of the Fe-Se-H compound
S. I. Bondarenko, A. A. Prokhorov, N. N. Galtsov et al.
Stabilization of Interband Phase Solitons in Two-Band Noncentrosymmetric Superconducting Rings
Yuriy Yerin, Boris Malomed, Stefan-Ludwig Drechsler et al.
Strain-driven orbital-selective reconstruction and bicollinear-to-stripe evolution in FeTe
Zhenfeng Ouyang, Yin Chen, Yi-Heng Tian et al.
Supercurrent detection and manipulation of topological phase transitions in Shiba-Majorana hybrid systems
Debika Debnath, Ioannis Ioannidis, Paramita Dutta et al.
Exact pair density wave in topological moire flat bands and universal superfluid stiffness
Zhengzhi Wu, Ming-rui Li, Hong Yao
Electrical manipulation of oxygen stoichiometry in multiterminal YBa2Cu3O7-δ junctions
Daniel Stoffels, Caio C. Quaglio-Gomes, Nicolas Lejeune et al.